Holey electrode grids for photovoltaic cells with subwavelength and superwavelength feature sizes

ABSTRACT

A photovoltaic cell and a method of forming an electrode grid on a photovoltaic semiconductor substrate of a photovoltaic cell are disclosed. In one embodiment, the photovoltaic cell comprises a photovoltaic semiconductor substrate; a back electrode electrically connected to a back surface of the substrate; and a front electrode electrically connected to a front surface of the substrate. The substrate, back electrode, and front electrode form an electric circuit for generating an electric current when said substrate absorbs light. The front electrode is comprised of a metal grid defining a multitude of holes. These holes may be periodic, aperiodic, or partially periodic. The front electrode may be formed by depositing nanospheres on the substrate; forming a metallic layer on the substrate, around the nanospheres; and removing the nanospheres, leaving an electrode grid defining a multitude of holes on the substrate.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention generally relates to solar or light energy, and more specifically, the invention relates to photovoltaic cells.

2. Background Art

Solar energy has long been looked to as a significant part of a solution to the ever increasing energy needs of the planet's population. Increasing costs of mining fossil fuels and increased concerns over “greenhouse” emissions have furthered interest in exploiting alternative energy strategies, including solar energy sources. To date, solar energy conversion has generally relied upon either the direct harvesting of solar thermal energy, e.g., in heating applications, or in thermoelectric conversion, or through the direct conversion of photonic energy to electrical energy through the use of photovoltaic cells.

Photovoltaic cells have developed according to two distinct methods. The initial operational cells employed a matrix of single crystal silicon appropriately doped to produce a planar p-n junction. An intrinsic electric field established at the p-n junction produces a voltage by directing solar photon produced holes and free electrons in opposite directions. Despite good conversion efficiencies and long-term reliability, widespread energy collection using single-crystal silicon cells is thwarted by the exceptionally high cost of single crystal silicon material and interconnection processing.

A second approach to produce photovoltaic cells is by depositing thin photovoltaic semiconductor films on a supporting substrate. Material requirements are minimized and technologies can be proposed for mass production. The thin film structures can be designed according to doped homojunction technology such as that involving silicon films, or can employ heterojunction approaches such as those using CdTe or chalcopyrite materials. Despite significant improvements in individual cell conversion efficiencies for both single crystal and thin film approaches, photovoltaic energy collection has been generally restricted to applications having low power requirements.

In all solar cells, especially the high performance ones, series resistance issue is a serious limiting factor for cell performance. This series resistance is associated with the contact electrode geometry, emitter (top) layer sheet resistance, and metal-semiconductor contact resistance. The design of the electrode structure must consider the trade off between area coverage and the shadowing loss. A standard approach is to use comb-like metal grids or to use transparent conducting oxide (TCO) film that combines transparency and good conductivity of the film. However such TCO film still has a limited conductivity and still contributes to considerable amount of series resistance.

BRIEF SUMMARY

Embodiments of the invention provide a photovoltaic cell and a method of forming an electrode grid on a photovoltaic semiconductor substrate of a photovoltaic cell. In one embodiment, the photovoltaic cell comprises a photovoltaic semiconductor substrate having a front, light receiving surface, and a back surface; a back electrode electrically connected to said back surface; and a front electrode electrically connected to the front surface. The substrate, back electrode, and front electrode form an electric circuit for generating an electric current when said substrate absorbs light. The front electrode is comprised of a metal grid defining a multitude of holes having widths less than 1000 nms.

In one embodiment, the holes of the front electrode form a periodic pattern in the front electrode, and for example, this pattern may repeat with a period between 200 nms and 50 ums. In another embodiment, the holes of the front electrode form an aperiodic pattern in said front electrode. In another embodiment, the holes in the front electrode form a partially periodic pattern in said front electrode.

In one embodiment, the holes in the front electrode have circular shapes with diameters between 100 and 1000 nms. In one embodiment, the photovoltaic cell is for use with light at a wavelength λ, and said multitude of holes in the front electrode have widths greater than λ. In another embodiment, the photovoltaic cell is for use with light at a wavelength λ, and the multitude of holes in the front electrode have widths less than λ. In another embodiment, the photovoltaic cell is for use with light at a wavelength λ, and some of the holes in the front electrode have widths greater than λ, while others of these holes have widths less than λ. In one embodiment, the front electrode extends over a defined area of the front surface of said substrate, and the holes of the front electrode cover more than 80% of said defined area.

In one embodiment of the invention, a method is provided for forming an electrode grid on a photovoltaic semiconductor substrate. In one embodiment, the method comprises depositing a quantity of nanoshperes on said substrate; forming a metallic layer on the substrate, around said nanospheres; and removing said nanoshperes, whereby an electrode grid defining a multitude of holes is left on the substrate, electrically connected thereto.

In one embodiment, the depositing includes forming a monolayer of the nanospheres on said substrate. In an embodiment, the depositing includes trimming said nanospheres to a desired size; and, for example, this trimming may be done using O₂. In one embodiment, said forming includes depositing a layer of a metal on the substrate and the nanospheres. In an embodiment, said removing includes lifting the nanospheres off said substrate; and, for example, this may be done by peeling the nanoshperes off said substrate using a tape and cleaning the substrate in a hot solvent such as acetone or NMP (N-Methyl-2-pyrrolidone)

Embodiments of the invention use metal electrode to retain its very high conductivity (˜100× larger than best TCO), patterned into holey structures with subwavelength or superwavelength feature size while maintaining the same level of shadowing loss. Depending on the size of the holes and their periodicity, the invention can achieve significant benefits such as: reduced cell series resistance, as the metal grid has larger area coverage so the current transport are not limited by the (high) emitter sheet resistance anymore, and enhanced light transmission due to subwavelength electrode linewidth (that is invisible to light) or due to plasmonics effect.

BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWINGS

FIG. 1 is a diagram of a photovoltaic device.

FIG. 2( a) illustrates the impact of varying electrode thickness to the efficiency of a photovoltaic cell.

FIG. 2( b) illustrates the components of the overall series resistance of a photovoltaic cell.

FIG. 3 illustrated the principle of replacing the fingers of a photovoltaic cell with a holey electrode grid.

FIG. 4( a) shows the enhanced transmission effect through an array of holes of subwavelength size.

FIG. 4( b) shows experimental data for various hole sizes.

FIG. 5 illustrates a fabrication process of a holey electrode grid.

FIG. 6 shows fabrication steps that may be used in the fabrication process.

FIG. 7( a) shows an etch timing diagram for trimming the sizes of nanospheres in the fabrication process.

FIG. 7( b) illustrates two electrode grids that may be formed using the process of FIGS. 5 and 6.

FIG. 8 shows a metal grid on Silicon substrate fabricated using nanosphere lithography.

DETAILED DESCRIPTION

FIG. 1 is a diagram of a photovoltaic (PV) device, or solar cell, 10. The PV device 10 includes a back electrode layer 12, a PV material 14 and a front electrode 16. Light energy is transmitted to the PV layer 14, where it is absorbed and transformed into electric energy. The electricity generated within the PV device 10 migrates to either the front electrode 16 or the back electrode 12, from where it is directed out of the cell through an electrical contact 20 or 22. The PV layer 14 may be constructed of any among many different types of materials, including, but not limited to, semiconductor junctions, organic-dye based materials, photoelectrochemical cells, polymer solar cells, nanocrystal solar cells or dye sensitized solar cells, as well as other PV cell technologies.

More specifically, in the device of FIG. 1, the PV material 14 may be a semiconductor substrate comprised of a polycrystalline silicon but can also be a single-crystalline silicon, and it is of a p-type with, for example, an impurity concentration of 5×10¹⁶ cm⁻³ with boron as the impurity, for example. The thickness of this semiconductor substrate 14 may be from 1 μm to 150 μm. An aluminum oxide (Al₂O₃) diffuse-reflection substrate (not shown) that is 800 μm thick, for example, may be adhered to the back surface of the semiconductor substrate 14.

As mentioned above, series resistance associated with the contact electrode is a serious limiting factor for high performance solar cells. FIG. 2( a) illustrates the impact of the varying electrode thickness (or the electrode series resistance) to the cell efficiency. Thus engineering an optimum contact electrode is critical in achieving peak performance for all type solar cells.

The overall cell series resistance originates mainly from three components as shown in FIG. 2( b): emitter layer resistance (R_(E)), electrode (busbar and finger) resistance R_(BF) and the electrode-semiconductor contact resistance (R_(C)). Other than these factors, the shadowing loss due to the electrode coverage (typically ˜10%) also accounts for the loss of the cell performance. These series resistances could be reduced by increasing the area coverage but this will increase the shadowing loss. One could also make the electrode thicker, but this is often limited by the deposition technique.

Ideally a solar cell needs a contact electrode that is transparent but highly conductive to minimize the shadowing loss and series resistance losses. One attempt is to use transparent conducting oxide film such as indium tin oxide (typical transmission ˜80% and sheet resistance ˜20 Ω/sq). The present invention provides an alternative technique, utilizing an electrode grid that reduces both series resistance and effectively reduces the shadowing loss of the electrode.

With reference to FIG. 3, in accordance with an embodiment of this invention, the finger electrode 30 is replaced with a “holey” metal grid 32 with small feature size while keeping the same shadowing factor. The grid 32 can have holes 34 with both subwavelength dimensions (w<λ), as well as superwavelength dimensions (w>λ). The hole pattern may be periodic, may be aperiodic, or may be partially periodic. In the case of periodicity, the lattice period α may be, for example, ˜200 nm to ˜50 μm.

Such an electrode structure 32 provides important advantages. One significant advantage is reduced emitter series resistance (R_(E)), since the current path from the junction to the electrode are reduced. E.g. typical finger spacing of solar cell is 500 μm and the emitter series resistance scales with this value. By having a metal grid 32 with very small lattice spacing (e.g. in order of μm) the series resistance can be reduced significantly. Another important advantage is that, in the case where the hole dimensions are larger than the wavelength of light (w>λ), the metal will cover <20% of the area, resulting in >80% transmission. At the same time, the conductivity of the film will be high. As a result, these conducting holey films can be used both for thin film PV (as a replacement for ITO or doped ZnO) and for crystalline silicon. In the case of crystalline Si, since the lateral path for the minority carrier in the silicon is shorter, it is possible to dope the emitter to lower values, thereby improving minority carrier lifetimes in the emitter.

In the case where the hole dimension is smaller than the light wavelength (w<λ), since the grid has linewidth smaller than the wavelength of light, the grid lines will be less visible to the incoming light or the reflection will be reduced. This effectively reduces the shadowing loss due to the reflection of the electrode. Further, when the grid lattice period is smaller than the light's wavelength (α<λ), embodiments of the invention can exploit a plasmonics effect of enhanced transmission phenomena through an array of subwavelength holes. This effect occurs because the periodicity of the metal structure helps to couple the light and the surface plasmons more effectively and reradiate the light energy as transmitted light. This feature is illustrated in FIGS. 4( a) and 4(b). This effect could also potentially reduce the shadowing loss due to the electrode.

Fabrication of a structure with submicron structures over a large area is prohibitively expensive using standard lithography technique (deep UV or electron beam lithography). Thus a nanosphere lithography technique may be used to realize large scale but low cost patterning of a subwavelength metal grid for solar cell application.

FIGS. 5 and 6 illustrate, as an example, a fabrication process that may be used to form the holey electrode grid. In this process, at step 42, the nanospheres (NS) colloid is prepared with proper dilution with methanol (added with surfactant Triton-X 100 by 1:400 volume) to achieve monolayer deposition. The amount is, in one embodiment, determined experimentally (e.g. for 500 nm NSs NS:methanol=7:5 volume). At step 46, the nanospheres 48 are spun on the substrate 50, as shown at 52. The size of the NS are trimmed at step 54 to the desired size using O₂ plasma. The etch timing data is shown in FIG. 7( a). At step 56, metal 60 is deposited onto the substrate. At step 62, the NSs are lifted off the substrate. This may be done by first peeling the NSs off using tape and then cleaning using NMP (N-Methyl-2-pyrrolidone).

A result of a metal grid 64 made by nanosphere lithography is shown in FIG. 8. Note that the holes filling factor can be controlled by controlling the size of the NSs with O₂ plasma trimming process as shown at 66 in FIG. 7( b). A larger filling factor means smaller shadowing loss. For a closely packed NS lattice as shown in FIG. 7( b), the minimum shadowing factor (area covered by metal) is 1-√{square root over (3)} π/2 or 9.3%. However since the feature size of the metal lines are smaller than the wavelength of light, the effective shadowing loss will be smaller.

While it is apparent that the invention herein disclosed is well calculated to fulfill the objects stated above, it will be appreciated that numerous modifications and embodiments may be devised by those skilled in the art, and it is intended that the appended claims cover all such modifications and embodiments as fall within the true spirit and scope. 

1. A photovoltaic cell comprising: a photovoltaic semiconductor substrate having a front, light receiving surface, and a back surface; a back electrode electrically connected to said back surface; and a front electrode electrically connected to the front surface; wherein the substrate, back electrode, and front electrode form an electric circuit for generating an electric current when said substrate absorbs light; and wherein said front electrode is comprised of a metal grid defining a multitude of holes having widths less than 1000 nms.
 2. The photovoltaic cell according to claim 1, wherein said holes form a periodic pattern is said front electrode.
 3. The photovoltaic cell according to claim 2, wherein said pattern repeats with a period between 200 nms and 50 ums.
 4. The photovoltaic cell according to claim 1, wherein said holes form an aperiodic pattern in said front electrode.
 5. The photovoltaic cell according to claim 1, wherein said holes form a partially periodic pattern in said front electrode.
 6. The photovoltaic cell according to claim 1, wherein said holes have circular shapes with diameters between 100 and 1000 nms.
 7. The photovoltaic cell according to claim 1, for use with light at a wavelength, and wherein said multitude of holes have widths greater than.
 8. The photovoltaic cell according to claim 1, for use with light at a wavelength, and wherein said multitude of holes have widths less than.
 9. The photovoltaic cell according to claim 1, for use with light at a wavelength, and wherein some of said multitude of holes have widths greater than, and others of said multitude of holes have widths less than.
 10. The photovoltaic cell according to claim 1, wherein said front electrode extends over a defined area of the front surface of said substrate, and said holes cover more than 80% of said defined area.
 11. A method of forming an electrode grid on a photovoltaic semiconductor substrate, comprising: depositing a quantity of nanoshperes on said substrate; forming a metallic layer on the substrate, around said nanospheres; and removing said nanoshperes, whereby an electrode grid defining a multitude of holes is left on the substrate electrically connected thereto.
 12. The method according to claim 11, wherein the depositing includes forming a monolayer of the nanospheres on said substrate.
 13. The method according to claim 11, wherein said depositing includes trimming said nanospheres to a desired size.
 14. The method according to claim 13, wherein said trimming includes trimming said nanospheres using O2.
 15. The method according to claim 11, wherein said forming includes depositing a layer of a metal on the substrate and the nanospheres.
 16. The method according to claim 11, wherein said removing includes lifting the nanospheres off said substrate.
 17. The method according to claim 16, wherein said lifting includes peeling the nanoshperes off said substrate using a tape.
 18. A photovoltaic cell comprising: a photovoltaic semiconductor substrate having a front, light receiving surface, and a back surface; a back electrode electrically connected to said back surface; and a front electrode electrically connected to the front surface; wherein the substrate, back electrode, and front electrode form an electric circuit for generating an electric current when said substrate absorbs light; and wherein said front electrode is comprised of a metal grid attached to said front surface and defining a multitude of circular openings having diameters less than 1000 nms and forming a periodic pattern in said grid having a period of between 200 nms and 50 μms.
 19. The photovoltaic cell according to claim 18 for converting photonic energy to said electrical current, said photonic energy having a defined average operating wavelength, and wherein said period is less than the average operating wavelength to enable a plasmonics effect of enhanced transmission phenomena of light through said openings.
 20. The photovoltaic cell according to claim 18, wherein the diameters of said openings are less than 700 nm to reduce shadowing loss due to reflection of the front electrode. 